Performance of a Degassing Cyclone with Main and Subsidiary Chambers

Based on the premise that large bubbles are removed in larger cyclones and small bubbles in smaller cyclones, a combined degassing cyclone with main and subsidiary chambers was designed to enhance liquid degassing. The pressure loss, liquid flow rate at the gas outlet, split ratio, gas flow rate at the liquid outlet, and degassing efficiency of the degassing cyclone were measured and calculated. Pressure loss correlations were established which relates the Euler number to the gas and liquid Reynolds numbers in the main chamber. Most cases exhibit a degassing efficiency greater than 0.998 when the liquid flow rate is more than 0.7 m³h^?1. The contours of pressure loss, split ratio, and degassing efficiency provide an effective guidance for designing a degassing cyclone.     

基于SVD和SSA-VMD降噪的轴承故障特征提取

针对强噪声背景下轴承故障特征提取困难的问题，提出一种基于奇异值分解和参数优化变分模态分解联合降噪的轴承故障特征提取方法(SSVMD)：首先，对原始信号进行奇异值分解(Singular Value Decomposition，SVD)处理，运用奇异值差分谱法选取有效奇异值并将原始信号重构得到初步降噪信号；其次，为防止故障信息丢失，将残余信号进行麻雀算法(Sparrow Search Algorithm，SSA)优化的变分模态分解(Variational Mode Decomposition，VMD）算法处理，得到最佳的模态个数K和惩罚参数α，选取峭度值最大、包络熵最小的IMF分量与初步降噪信号叠加得到最终降噪信号，并对信号进行包络分析；最后，通过仿真和试验数据分析得出，该方法能在信噪比很低的情况下降低噪声含量并提取轴承故障特征，为设备的状态监测和故障诊断提供理论依据。     

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

The chromium-promoted preparation of forsterite refractory materials from ferronickel slag was investigated by microwave sintering of the slag with the additions of sintered magnesia and 0–10 wt% chromium oxide (Cr₂O₃). The thermodynamic calculations revealed that the addition of Cr₂O₃ can promote the formations of spinel and liquid phase and maintain high content of forsterite below 1500 °C. The experimental results showed that there existed a stronger promoting effect of Cr₂O₃ additive on the properties of refractory materials in the microwave field than that in conventional sintering. It was attributed to the preferential formation and growth of spinel with stronger microwave absorption than other phases (e.g., enstatite), the existence of more forsterite, and the enhanced densification in association with the presence of more liquid phase at the same temperature. By microwave sintering of the mixture of ferronickel slag, 25 wt% sintered magnesia, and 4 wt% Cr₂O₃ at 1350 °C for 20 min, a superior refractory material with refractoriness of 1801 °C, thermal shock resistance of 6 times, bulk density of 2.97 g/cm³, apparent porosity of 1.4%, and compressive strength of 197 MPa was obtained. Compared with that prepared by conventional sintering at 1350 °C for 2 h, the refractoriness and thermal shock resistance were increased by 175 °C and 100%, respectively. The present study provided a novel method for preparing high-quality refractory materials from ferronickel slag and relevant industrial wastes.     

基础油中金刚石纳米颗粒润滑性能和导热性能的分子动力学分析*

为了研究纳米颗粒对基础油液热导率的影响,在基础油蓖麻油酸中加入不同体积分数和粒径的纳米金刚石颗粒,采用LAMMPS和分子动力学的研究方法,对粒子数密度以及粒子的径向分布规律、导热系数进行研究。结果表明:加入纳米颗粒的纳米流体的热物理性质受到多方面的影响,其中包括纳米颗粒体积分数及粒径等;随纳米粒子体积分数的提高纳米流体的热导率呈近似线性增加,随着纳米粒子粒径的减小,纳米粒子润滑膜的承载能力增强。纳米润滑膜能承受很高的外界冲击力,这有助于减小两作用面之间的摩擦,减小表面磨损;加入纳米颗粒的润滑油会减小摩擦副之间的摩擦和增强散热,提高热导率。     

全液相高温调剖剂的研制

针对汽驱开发试验中出现的汽窜、油层受效不均等问题,研制出一种全液相高温调剖剂,10 g堵剂沉淀量达到1.8 g,无机凝胶强度达到5 MPa/m,封堵率在55％ ～90％间可调,耐温达到350℃,经现场调剖试验后,措施井的注汽压力提高1.7 MPa,吸汽剖面改善明显,调剖效果显著,提高了汽驱的注汽利用率和采收率.